A sol-gel method for preparing oriented YBa2Cu3O 7- delta films on silver substrates

M. L. Kullberg, Michael T. Lanagan, W. Wu, R. B. Poeppel

Research output: Contribution to journalArticle

23 Citations (Scopus)

Abstract

YBa2Cu3O7- delta (YBCO) superconducting films on polycrystalline silver substrates have been fabricated using a sol-gel/spray pyrolysis method. The sol-gel precursor is composed of yttrium, barium and copper acetates that are dissolved in a minimum amount of water and partially gelled using ethanolamine. Silver substrates were heated to 300 degrees C before spray-coating with the precursor solution. Intermittent treatment of films at 550 degrees C in air between spray coats resulted in dense films. Subsequently, the YBCO films were sintered between 850 and 950 degrees C and oxygen annealed on cool down. Film thicknesses of 1-3 mu m were obtained and were highly oriented with the c axis perpendicular to the silver surface. Critical current densities (Jc) of 200-500 A cm-2 have been measured at 77 K and no applied magnetic field; higher Jc values have been measured on films with many pin holes, which appear to increase the number of oxygen entry points into the oriented films. The Jc rapidly decreases in magnetic field, which indicates that transport properties are dominated by weak-link behaviour.

Original languageEnglish (US)
Article number003
Pages (from-to)337-342
Number of pages6
JournalSuperconductor Science and Technology
Volume4
Issue number8
DOIs
StatePublished - Dec 1 1991

Fingerprint

Silver
Sol-gel process
silver
gels
sprayers
Substrates
Sol-gels
Magnetic fields
Oxygen
Ethanolamines
Yttrium
Superconducting films
Ethanolamine
Spray pyrolysis
superconducting films
oxygen
Barium
yttrium
magnetic fields
entry

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Condensed Matter Physics
  • Metals and Alloys
  • Electrical and Electronic Engineering
  • Materials Chemistry

Cite this

@article{1f4ae2e3fc5a4b9d894a5b50ab268c15,
title = "A sol-gel method for preparing oriented YBa2Cu3O 7- delta films on silver substrates",
abstract = "YBa2Cu3O7- delta (YBCO) superconducting films on polycrystalline silver substrates have been fabricated using a sol-gel/spray pyrolysis method. The sol-gel precursor is composed of yttrium, barium and copper acetates that are dissolved in a minimum amount of water and partially gelled using ethanolamine. Silver substrates were heated to 300 degrees C before spray-coating with the precursor solution. Intermittent treatment of films at 550 degrees C in air between spray coats resulted in dense films. Subsequently, the YBCO films were sintered between 850 and 950 degrees C and oxygen annealed on cool down. Film thicknesses of 1-3 mu m were obtained and were highly oriented with the c axis perpendicular to the silver surface. Critical current densities (Jc) of 200-500 A cm-2 have been measured at 77 K and no applied magnetic field; higher Jc values have been measured on films with many pin holes, which appear to increase the number of oxygen entry points into the oriented films. The Jc rapidly decreases in magnetic field, which indicates that transport properties are dominated by weak-link behaviour.",
author = "Kullberg, {M. L.} and Lanagan, {Michael T.} and W. Wu and Poeppel, {R. B.}",
year = "1991",
month = "12",
day = "1",
doi = "10.1088/0953-2048/4/8/003",
language = "English (US)",
volume = "4",
pages = "337--342",
journal = "Superconductor Science and Technology",
issn = "0953-2048",
publisher = "IOP Publishing Ltd.",
number = "8",

}

A sol-gel method for preparing oriented YBa2Cu3O 7- delta films on silver substrates. / Kullberg, M. L.; Lanagan, Michael T.; Wu, W.; Poeppel, R. B.

In: Superconductor Science and Technology, Vol. 4, No. 8, 003, 01.12.1991, p. 337-342.

Research output: Contribution to journalArticle

TY - JOUR

T1 - A sol-gel method for preparing oriented YBa2Cu3O 7- delta films on silver substrates

AU - Kullberg, M. L.

AU - Lanagan, Michael T.

AU - Wu, W.

AU - Poeppel, R. B.

PY - 1991/12/1

Y1 - 1991/12/1

N2 - YBa2Cu3O7- delta (YBCO) superconducting films on polycrystalline silver substrates have been fabricated using a sol-gel/spray pyrolysis method. The sol-gel precursor is composed of yttrium, barium and copper acetates that are dissolved in a minimum amount of water and partially gelled using ethanolamine. Silver substrates were heated to 300 degrees C before spray-coating with the precursor solution. Intermittent treatment of films at 550 degrees C in air between spray coats resulted in dense films. Subsequently, the YBCO films were sintered between 850 and 950 degrees C and oxygen annealed on cool down. Film thicknesses of 1-3 mu m were obtained and were highly oriented with the c axis perpendicular to the silver surface. Critical current densities (Jc) of 200-500 A cm-2 have been measured at 77 K and no applied magnetic field; higher Jc values have been measured on films with many pin holes, which appear to increase the number of oxygen entry points into the oriented films. The Jc rapidly decreases in magnetic field, which indicates that transport properties are dominated by weak-link behaviour.

AB - YBa2Cu3O7- delta (YBCO) superconducting films on polycrystalline silver substrates have been fabricated using a sol-gel/spray pyrolysis method. The sol-gel precursor is composed of yttrium, barium and copper acetates that are dissolved in a minimum amount of water and partially gelled using ethanolamine. Silver substrates were heated to 300 degrees C before spray-coating with the precursor solution. Intermittent treatment of films at 550 degrees C in air between spray coats resulted in dense films. Subsequently, the YBCO films were sintered between 850 and 950 degrees C and oxygen annealed on cool down. Film thicknesses of 1-3 mu m were obtained and were highly oriented with the c axis perpendicular to the silver surface. Critical current densities (Jc) of 200-500 A cm-2 have been measured at 77 K and no applied magnetic field; higher Jc values have been measured on films with many pin holes, which appear to increase the number of oxygen entry points into the oriented films. The Jc rapidly decreases in magnetic field, which indicates that transport properties are dominated by weak-link behaviour.

UR - http://www.scopus.com/inward/record.url?scp=36149029340&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=36149029340&partnerID=8YFLogxK

U2 - 10.1088/0953-2048/4/8/003

DO - 10.1088/0953-2048/4/8/003

M3 - Article

VL - 4

SP - 337

EP - 342

JO - Superconductor Science and Technology

JF - Superconductor Science and Technology

SN - 0953-2048

IS - 8

M1 - 003

ER -