Anodic deposition of colloidal iridium oxide thin films from hexahydroxyiridate(IV) solutions

Yixin Zhao, Nella M. Vargas-Barbosa, Emil A. Hernandez-Pagan, Thomas E. Mallouk

Research output: Contribution to journalArticle

84 Scopus citations

Abstract

A facile, in-situ deposition route to stable iridium oxide (IrO x·nH2O) nanoparticle thin films from [Ir(OH) 6]2- solutions is reported. The [Ir(OH)6] 2- solution, made by alkaline hydrolysis of [IrCl6] 2-, is colorless and stable near neutral pH, and forms blue IrO x·nH2O nanoparticle suspensions once it is adjusted to acidic or basic conditions. IrOx·nH2O nanoparticle thin films are grown anodically on glassy carbon, fluorine-doped tin oxide, and gold electrodes by electrolyzing [Ir(OH)6] 2- solutions at +1.0-1.3 V versus Ag/AgCl. The thickness of the IrOx·nH2O films can be controlled by varying the concentration of [Ir(OH)6]2-, the deposition potential, and/or the deposition time. These thin films are stable between pH 1 and 13 and have the lowest overpotential (η) for the oxygen evolution reaction (OER) of any yet reported. Near neutral pH, the Tafel slope for the OER at a IrOx·nH2O film/Au rotating disk electrode was 37-39 mV per decade. The exchange current density for the OER was 4-8 × 10-10 A cm-2 at a 4 mC cm-2 coverage of electroactive Ir.

Original languageEnglish (US)
Pages (from-to)2087-2093
Number of pages7
JournalSmall
Volume7
Issue number14
DOIs
StatePublished - Jul 18 2011

All Science Journal Classification (ASJC) codes

  • Biotechnology
  • Biomaterials
  • Chemistry(all)
  • Materials Science(all)

Fingerprint Dive into the research topics of 'Anodic deposition of colloidal iridium oxide thin films from hexahydroxyiridate(IV) solutions'. Together they form a unique fingerprint.

  • Cite this

    Zhao, Y., Vargas-Barbosa, N. M., Hernandez-Pagan, E. A., & Mallouk, T. E. (2011). Anodic deposition of colloidal iridium oxide thin films from hexahydroxyiridate(IV) solutions. Small, 7(14), 2087-2093. https://doi.org/10.1002/smll.201100485