Carbon deposition on Ni-based catalyst with TiO2 as additive during the syngas methanation process in a fluidized bed reactor

Fei Feng, Guohui Song, Jun Xiao, Laihong Shen, Sarma V. Pisupati

Research output: Contribution to journalArticle

Abstract

Syngas methanation is a crucial step in industry to produce synthetic natural gas, but the Ni-based catalysts for this reaction often deactivate severely because of carbon formation. Tests were carried out in a pressurized fluidized bed methanation reactor in order to analyze the carbon deposition on the nickel-based methanation catalysts with TiO2 as additive (Ni-Ti/Al2O3) and a conventional Ni-based catalyst (Ni/Al2O3). Test results showed that Ni-Ti/Al2O3 performed better compared to Ni/Al2O3. At higher operating temperature (823 K), CO conversion on Ni-Ti/Al2O3 was 13.6% higher than that on Ni/Al2O3, CH4 yield was 39.7% higher and CH4 selectivity was even 64.7% higher for Ni-Ti/Al2O3 compared to Ni/Al2O3. The raw and spent catalysts were characterized with XRD, EDS and N2 adsorption-desorption measurements to describe the carbon deposits on them. The characterization results indicated that elemental carbon appeared on the surface of the catalysts after methanation reaction and with the increase in reaction temperature, the carbon deposition was getting more serious. The deposited carbon blocked the tiny porous channels of the catalysts and caused a drastic change in the surface topography, which led to the degradation of the catalysts’ performance. The TiO2 additive provided a physical barrier to hydrocarbon adsorption and decomposition on the catalyst surface and the oxygen vacancies on Ni-Ti/Al2O3 acted as the active sites to promote the removal carbon on the Ni particles. Thus, the TiO2 additive can enhance the anti-coking properties and catalytic activity of Ni-Ti/Al2O3 compared to Ni/Al2O3. These findings aid in further improvement and optimization of highly carbon-resistant catalysts.

LanguageEnglish (US)
Pages85-91
Number of pages7
JournalFuel
Volume235
DOIs
StatePublished - Jan 1 2019

Fingerprint

Methanation
Fluidized beds
Carbon
Catalysts
Coking properties
Adsorption
Surface topography
Oxygen vacancies
Carbon Monoxide
Hydrocarbons
Nickel
titanium nickelide
Energy dispersive spectroscopy
Catalyst activity
Desorption
Natural gas
Deposits
Decomposition
Degradation
Temperature

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Fuel Technology
  • Energy Engineering and Power Technology
  • Organic Chemistry

Cite this

@article{23d5dc3a5f4447a0b2d5f306d62e6682,
title = "Carbon deposition on Ni-based catalyst with TiO2 as additive during the syngas methanation process in a fluidized bed reactor",
abstract = "Syngas methanation is a crucial step in industry to produce synthetic natural gas, but the Ni-based catalysts for this reaction often deactivate severely because of carbon formation. Tests were carried out in a pressurized fluidized bed methanation reactor in order to analyze the carbon deposition on the nickel-based methanation catalysts with TiO2 as additive (Ni-Ti/Al2O3) and a conventional Ni-based catalyst (Ni/Al2O3). Test results showed that Ni-Ti/Al2O3 performed better compared to Ni/Al2O3. At higher operating temperature (823 K), CO conversion on Ni-Ti/Al2O3 was 13.6{\%} higher than that on Ni/Al2O3, CH4 yield was 39.7{\%} higher and CH4 selectivity was even 64.7{\%} higher for Ni-Ti/Al2O3 compared to Ni/Al2O3. The raw and spent catalysts were characterized with XRD, EDS and N2 adsorption-desorption measurements to describe the carbon deposits on them. The characterization results indicated that elemental carbon appeared on the surface of the catalysts after methanation reaction and with the increase in reaction temperature, the carbon deposition was getting more serious. The deposited carbon blocked the tiny porous channels of the catalysts and caused a drastic change in the surface topography, which led to the degradation of the catalysts’ performance. The TiO2 additive provided a physical barrier to hydrocarbon adsorption and decomposition on the catalyst surface and the oxygen vacancies on Ni-Ti/Al2O3 acted as the active sites to promote the removal carbon on the Ni particles. Thus, the TiO2 additive can enhance the anti-coking properties and catalytic activity of Ni-Ti/Al2O3 compared to Ni/Al2O3. These findings aid in further improvement and optimization of highly carbon-resistant catalysts.",
author = "Fei Feng and Guohui Song and Jun Xiao and Laihong Shen and Pisupati, {Sarma V.}",
year = "2019",
month = "1",
day = "1",
doi = "10.1016/j.fuel.2018.07.076",
language = "English (US)",
volume = "235",
pages = "85--91",
journal = "Fuel",
issn = "0016-2361",
publisher = "Elsevier BV",

}

Carbon deposition on Ni-based catalyst with TiO2 as additive during the syngas methanation process in a fluidized bed reactor. / Feng, Fei; Song, Guohui; Xiao, Jun; Shen, Laihong; Pisupati, Sarma V.

In: Fuel, Vol. 235, 01.01.2019, p. 85-91.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Carbon deposition on Ni-based catalyst with TiO2 as additive during the syngas methanation process in a fluidized bed reactor

AU - Feng, Fei

AU - Song, Guohui

AU - Xiao, Jun

AU - Shen, Laihong

AU - Pisupati, Sarma V.

PY - 2019/1/1

Y1 - 2019/1/1

N2 - Syngas methanation is a crucial step in industry to produce synthetic natural gas, but the Ni-based catalysts for this reaction often deactivate severely because of carbon formation. Tests were carried out in a pressurized fluidized bed methanation reactor in order to analyze the carbon deposition on the nickel-based methanation catalysts with TiO2 as additive (Ni-Ti/Al2O3) and a conventional Ni-based catalyst (Ni/Al2O3). Test results showed that Ni-Ti/Al2O3 performed better compared to Ni/Al2O3. At higher operating temperature (823 K), CO conversion on Ni-Ti/Al2O3 was 13.6% higher than that on Ni/Al2O3, CH4 yield was 39.7% higher and CH4 selectivity was even 64.7% higher for Ni-Ti/Al2O3 compared to Ni/Al2O3. The raw and spent catalysts were characterized with XRD, EDS and N2 adsorption-desorption measurements to describe the carbon deposits on them. The characterization results indicated that elemental carbon appeared on the surface of the catalysts after methanation reaction and with the increase in reaction temperature, the carbon deposition was getting more serious. The deposited carbon blocked the tiny porous channels of the catalysts and caused a drastic change in the surface topography, which led to the degradation of the catalysts’ performance. The TiO2 additive provided a physical barrier to hydrocarbon adsorption and decomposition on the catalyst surface and the oxygen vacancies on Ni-Ti/Al2O3 acted as the active sites to promote the removal carbon on the Ni particles. Thus, the TiO2 additive can enhance the anti-coking properties and catalytic activity of Ni-Ti/Al2O3 compared to Ni/Al2O3. These findings aid in further improvement and optimization of highly carbon-resistant catalysts.

AB - Syngas methanation is a crucial step in industry to produce synthetic natural gas, but the Ni-based catalysts for this reaction often deactivate severely because of carbon formation. Tests were carried out in a pressurized fluidized bed methanation reactor in order to analyze the carbon deposition on the nickel-based methanation catalysts with TiO2 as additive (Ni-Ti/Al2O3) and a conventional Ni-based catalyst (Ni/Al2O3). Test results showed that Ni-Ti/Al2O3 performed better compared to Ni/Al2O3. At higher operating temperature (823 K), CO conversion on Ni-Ti/Al2O3 was 13.6% higher than that on Ni/Al2O3, CH4 yield was 39.7% higher and CH4 selectivity was even 64.7% higher for Ni-Ti/Al2O3 compared to Ni/Al2O3. The raw and spent catalysts were characterized with XRD, EDS and N2 adsorption-desorption measurements to describe the carbon deposits on them. The characterization results indicated that elemental carbon appeared on the surface of the catalysts after methanation reaction and with the increase in reaction temperature, the carbon deposition was getting more serious. The deposited carbon blocked the tiny porous channels of the catalysts and caused a drastic change in the surface topography, which led to the degradation of the catalysts’ performance. The TiO2 additive provided a physical barrier to hydrocarbon adsorption and decomposition on the catalyst surface and the oxygen vacancies on Ni-Ti/Al2O3 acted as the active sites to promote the removal carbon on the Ni particles. Thus, the TiO2 additive can enhance the anti-coking properties and catalytic activity of Ni-Ti/Al2O3 compared to Ni/Al2O3. These findings aid in further improvement and optimization of highly carbon-resistant catalysts.

UR - http://www.scopus.com/inward/record.url?scp=85050384283&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85050384283&partnerID=8YFLogxK

U2 - 10.1016/j.fuel.2018.07.076

DO - 10.1016/j.fuel.2018.07.076

M3 - Article

VL - 235

SP - 85

EP - 91

JO - Fuel

T2 - Fuel

JF - Fuel

SN - 0016-2361

ER -