Carbon-doped MgB2 thin films grown by hybrid physical-chemical vapor deposition

A. V. Pogrebnyakov, J. M. Redwing, J. E. Giencke, C. B. Eom, V. Vaithyanathan, D. G. Schlom, A. Soukiassian, S. B. Mi, C. L. Jia, J. Chen, Y. F. Hu, Y. Cui, Qi Li, X. X. Xi

Research output: Contribution to journalArticlepeer-review

10 Scopus citations

Abstract

Carbon-doped MgB2 thin films have been produced with hybrid physical-chemical vapor deposition (HPCVD) by adding a carbon-containing metalorganic magnesium precursor, bis(methylcyclopentadienyl)magnesium, to the carrier gas. The amount of the carbon added, thus the carbon content in the films, was controlled by the flow rate of a secondary hydrogen gas flow through the precursor bubbler. X-ray diffraction and electron microscopy showed that the carbon-doped MgB2 films are textured with c-axis oriented columnar nano-grains and highly resistive amorphous areas at the grain boundaries. When the amount of carbon in the films increases, the resistivity increases dramatically while Tc decreases much more slowly as the current-carrying cross section is reduced by the grain boundaries. The temperature-dependent part of the resistivity, Δρ = ρ(300 K) - ρ(50 K), increases only modestly until the highly resistive grain boundaries completely cut off the conducting path. The impact of the reduced cross section on critical current density Jc is discussed.

Original languageEnglish (US)
Pages (from-to)3321-3324
Number of pages4
JournalIEEE Transactions on Applied Superconductivity
Volume15
Issue number2 PART III
DOIs
StatePublished - Jun 2005

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Carbon-doped MgB<sub>2</sub> thin films grown by hybrid physical-chemical vapor deposition'. Together they form a unique fingerprint.

Cite this