Cold sintering of magnetic BaFe12O19 and other ferrites at 300 °C

Sarah Lowum, Richard D. Floyd, Yanglin Zhu, Zhiqiang Mao, Jon Paul Maria

Research output: Contribution to journalArticlepeer-review

Abstract

Densifying ZnFe2O4 and BaFe12O19 at 300 °C to values greater than 90% of theoretical is demonstrated via hydroflux-assisted densification (HAD), a derivative of the cold sintering process employing non-aqueous, flux-based mass transport phases to facilitate particle consolidation. Previous attempts to cold sinter these materials with aqueous-based mass transport phases were not as successful with final densities < 90%. Attempts to densify NiFe2O4 and (Ni0.5Zn0.5)Fe2O4 only achieved densities around 80%, indicating an alternative transport phase may be needed to achieve high densities in Ni-containing materials. Magnetic hysteresis measurements of the low-temperature densified BaFe12O19 samples produced magnetic saturation values as high as 93 emu/g and coercive fields as high as 1789 Oe, which are comparable to values reported in the literature for this material produced via other processing techniques. Additional techniques are suggested to further optimize the magnetic properties of BaFe12O19 densified following the HAD approach.

Original languageEnglish (US)
Pages (from-to)11229-11236
Number of pages8
JournalJournal of Materials Science
Volume56
Issue number19
DOIs
StatePublished - Jul 2021

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Cold sintering of magnetic BaFe<sub>12</sub>O<sub>19</sub> and other ferrites at 300 °C'. Together they form a unique fingerprint.

Cite this