Dielectric and piezoelectric properties of Fe2O3-doped 0.57PSN-0.43PT ceramics

Jin Soo Kim, Yun Han Chen, Kenji Uchino

Research output: Contribution to journalArticle

3 Scopus citations

Abstract

Dielectric and piezoelectric properties of iron-doped 0.57Pb(Sc1/2Nb1/2)O3-0.43PbTiO3 were investigated. The maximum dielectric constant (ε330 = 2551) and the minimum dielectric loss (tanδ = 0.51%) at room temperature were obtained at 0.1 wt% and 0.3 wt% of Fe2O3 additions, respectively. The temperature dependence of the dielectric constant was measured between 20°C and 350°C. With the additions of Fe2O3, the piezoelectric constant d33 and electromechanical coupling factor kp were slightly decreased, but the mechanical quality factor Qm was significantly increased. The highest mechanical quality factor (Qm=297) was obtained at 0.3 wt% Fe2O3, which is 4.4 times larger than that of non-doped 0.57PSN-0.43PT ceramics.

Original languageEnglish (US)
Pages (from-to)S1248-S1250
JournalJournal of the Korean Physical Society
Volume32
Issue number3 SUPPL.
StatePublished - Dec 1 1998

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Dielectric and piezoelectric properties of Fe<sub>2</sub>O<sub>3</sub>-doped 0.57PSN-0.43PT ceramics'. Together they form a unique fingerprint.

  • Cite this