Durability and performance of press molded polymer composite monopolar plates

Vernon Webb, Michael Anthony Hickner, Donald Baird, John Lesko, Scott Case

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

The electrical and mechanical properties of new lightweight graphite polymeric separator plates aged in a PEM fuel cell were investigated to assess their resistance to short-term durability. While the changes in electrical properties of great interest to the operation of the fuel cell, mechanical and dimensional stability over the life of the cell are critical. Thus, new polymeric based separator plates developed at Virginia Tech were aged under standard operating conditions in a PEM fuel cell over 300 hours at low pressure and 85°C. A comparison of conductivity, stiffness and strength of aged plates was made to as manufactured and unaged plates. Over the aging period, electrical conductivity did not decline even as the fuel cell performance showed some changes as evidenced by polarization curves. However, the mechanical strength of the monopolar plates was observed to decline less than 10% after 300 hours of fuel cell operation, due to the lack of stability of the polyester resin used to facilitate the rapid manufacturing of these new plates. These property changes were found to be independent of aging on the reduction and oxidation sides. Further work continues on plates formed through both fiber wet lay technology and those produced by compression molding of unique graphite filled epoxy systems, and to improve the electrochemical performance of cells fabricated using the resulting plates to levels comparable to those observed when using existing plate materials.

Original languageEnglish (US)
Pages (from-to)35-41
Number of pages7
JournalScience and Engineering of Composite Materials
Volume12
Issue number1-2
StatePublished - Jun 14 2005

Fingerprint

Fuel cells
Polymers
Durability
Composite materials
Graphite
Separators
Electric properties
Aging of materials
Polyester resins
Compression molding
Mechanical stability
Dimensional stability
Strength of materials
Stiffness
Polarization
Oxidation
Mechanical properties
Fibers

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

Cite this

Webb, Vernon ; Hickner, Michael Anthony ; Baird, Donald ; Lesko, John ; Case, Scott. / Durability and performance of press molded polymer composite monopolar plates. In: Science and Engineering of Composite Materials. 2005 ; Vol. 12, No. 1-2. pp. 35-41.
@article{ae09bdbf273e4c64b9d0299913e16182,
title = "Durability and performance of press molded polymer composite monopolar plates",
abstract = "The electrical and mechanical properties of new lightweight graphite polymeric separator plates aged in a PEM fuel cell were investigated to assess their resistance to short-term durability. While the changes in electrical properties of great interest to the operation of the fuel cell, mechanical and dimensional stability over the life of the cell are critical. Thus, new polymeric based separator plates developed at Virginia Tech were aged under standard operating conditions in a PEM fuel cell over 300 hours at low pressure and 85°C. A comparison of conductivity, stiffness and strength of aged plates was made to as manufactured and unaged plates. Over the aging period, electrical conductivity did not decline even as the fuel cell performance showed some changes as evidenced by polarization curves. However, the mechanical strength of the monopolar plates was observed to decline less than 10{\%} after 300 hours of fuel cell operation, due to the lack of stability of the polyester resin used to facilitate the rapid manufacturing of these new plates. These property changes were found to be independent of aging on the reduction and oxidation sides. Further work continues on plates formed through both fiber wet lay technology and those produced by compression molding of unique graphite filled epoxy systems, and to improve the electrochemical performance of cells fabricated using the resulting plates to levels comparable to those observed when using existing plate materials.",
author = "Vernon Webb and Hickner, {Michael Anthony} and Donald Baird and John Lesko and Scott Case",
year = "2005",
month = "6",
day = "14",
language = "English (US)",
volume = "12",
pages = "35--41",
journal = "Science and Engineering of Composite Materials",
issn = "0334-181X",
publisher = "Walter de Gruyter GmbH & Co. KG",
number = "1-2",

}

Durability and performance of press molded polymer composite monopolar plates. / Webb, Vernon; Hickner, Michael Anthony; Baird, Donald; Lesko, John; Case, Scott.

In: Science and Engineering of Composite Materials, Vol. 12, No. 1-2, 14.06.2005, p. 35-41.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Durability and performance of press molded polymer composite monopolar plates

AU - Webb, Vernon

AU - Hickner, Michael Anthony

AU - Baird, Donald

AU - Lesko, John

AU - Case, Scott

PY - 2005/6/14

Y1 - 2005/6/14

N2 - The electrical and mechanical properties of new lightweight graphite polymeric separator plates aged in a PEM fuel cell were investigated to assess their resistance to short-term durability. While the changes in electrical properties of great interest to the operation of the fuel cell, mechanical and dimensional stability over the life of the cell are critical. Thus, new polymeric based separator plates developed at Virginia Tech were aged under standard operating conditions in a PEM fuel cell over 300 hours at low pressure and 85°C. A comparison of conductivity, stiffness and strength of aged plates was made to as manufactured and unaged plates. Over the aging period, electrical conductivity did not decline even as the fuel cell performance showed some changes as evidenced by polarization curves. However, the mechanical strength of the monopolar plates was observed to decline less than 10% after 300 hours of fuel cell operation, due to the lack of stability of the polyester resin used to facilitate the rapid manufacturing of these new plates. These property changes were found to be independent of aging on the reduction and oxidation sides. Further work continues on plates formed through both fiber wet lay technology and those produced by compression molding of unique graphite filled epoxy systems, and to improve the electrochemical performance of cells fabricated using the resulting plates to levels comparable to those observed when using existing plate materials.

AB - The electrical and mechanical properties of new lightweight graphite polymeric separator plates aged in a PEM fuel cell were investigated to assess their resistance to short-term durability. While the changes in electrical properties of great interest to the operation of the fuel cell, mechanical and dimensional stability over the life of the cell are critical. Thus, new polymeric based separator plates developed at Virginia Tech were aged under standard operating conditions in a PEM fuel cell over 300 hours at low pressure and 85°C. A comparison of conductivity, stiffness and strength of aged plates was made to as manufactured and unaged plates. Over the aging period, electrical conductivity did not decline even as the fuel cell performance showed some changes as evidenced by polarization curves. However, the mechanical strength of the monopolar plates was observed to decline less than 10% after 300 hours of fuel cell operation, due to the lack of stability of the polyester resin used to facilitate the rapid manufacturing of these new plates. These property changes were found to be independent of aging on the reduction and oxidation sides. Further work continues on plates formed through both fiber wet lay technology and those produced by compression molding of unique graphite filled epoxy systems, and to improve the electrochemical performance of cells fabricated using the resulting plates to levels comparable to those observed when using existing plate materials.

UR - http://www.scopus.com/inward/record.url?scp=19844368063&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=19844368063&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:19844368063

VL - 12

SP - 35

EP - 41

JO - Science and Engineering of Composite Materials

JF - Science and Engineering of Composite Materials

SN - 0334-181X

IS - 1-2

ER -