Effect of activator, curing and humidity on drying shrinkage of alkali-activated fly ash

Research output: Contribution to journalArticle

1 Scopus citations

Abstract

Alkali-activated fly ash (AAFA) concrete is receiving considerable attention due to its environmental benefits; however, its long-term performance still requires validation and laboratory verification. This research studied the drying shrinkage of AAFA pastes as a function of activator composition (water content and n-modulus), relative humidity (RH) and heat-curing duration. Four AAFAs activated by different sodium silicate solutions and a control ordinary Portland cement (OPC) were examined. The activating solution affected the pore structure, pore solution and shrinkage characteristics of AAFAs. Use of an activator with a higher n-modulus resulted in a finer pore structure, superior mechanical properties and a larger magnitude of shrinkage. The results indicate that heat-cured AAFA paste dried faster, and its shrinkage reached equilibrium earlier compared to that of OPC. Similar to OPC, a bilinear relationship between RH and shrinkage of AAFA was observed. The results indicate that a longer steam-curing duration can stabilize the matrix of AAFAs and reduce their shrinkage.

Original languageEnglish (US)
Pages (from-to)71-83
Number of pages13
JournalGreen Materials
Volume7
Issue number2
DOIs
StatePublished - Jan 7 2019

All Science Journal Classification (ASJC) codes

  • Pollution
  • Polymers and Plastics
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Effect of activator, curing and humidity on drying shrinkage of alkali-activated fly ash'. Together they form a unique fingerprint.

  • Cite this