Fabrication of highly textured fine-grained α-alumina by templated grain growth of nanoscale precursors

Yunfei Chang, Stephen Poterala, Doruk Yener, Gary Lynn Messing

Research output: Contribution to journalArticlepeer-review

21 Scopus citations

Abstract

[0001] textured alumina ceramics with a fine grain size were fabricated between 1400°C and 1600°C via templated grain growth (TGG) using fine alumina platelets (∼0.6 and ∼3 μm diameter) aligned by tape casting in either a 50 nm α-Al2O3 matrix powder, or in a seeded boehmite sol. The 3 μm templates could be readily aligned by tape casting in both matrices (orientation parameters r = 0.27 and 0.18, respectively), whereas 0.6 μm diameter templates were well aligned in the seeded boehmite sol only (r = 0.29). Improved alignment in boehmite sols is attributed to inorganic gelation, resulting in a strongly pseudo-plastic rheology that preserves template alignment against the influence of Brownian motion. The in situ formation of fine α-Al2O3 matrix after transformation in the seeded boehmite system results in a higher driving force for TGG and improves texture development. The combination of 3 μm templates with a seeded boehmite matrix results in extremely high texture qualities (texture fraction f = 0.97-0.99, r = 0.17) while maintaining a relatively fine grain size (5-10 μm in diameter and 1.5-3 μm in thickness). Although undoped samples can be fully textured at 1600°C, adding as little as ∼0.25 wt% CaO/SiO2 dopant improves TGG kinetics and yields full texture at 1400°C.

Original languageEnglish (US)
Pages (from-to)1390-1397
Number of pages8
JournalJournal of the American Ceramic Society
Volume96
Issue number5
DOIs
StatePublished - May 1 2013

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Fabrication of highly textured fine-grained α-alumina by templated grain growth of nanoscale precursors'. Together they form a unique fingerprint.

Cite this