Fabrication of MEMS tonpilz transducers

Q. F. Zhou, L. P. Wang, G. Gerber, R. Meyer, D. Van Tol, S. Tadigadapa, W. J. Hughes, S. Trolier-McKinstry

Research output: Contribution to journalConference articlepeer-review

3 Scopus citations

Abstract

Tonpilz transducers consist of a heavy tail mass, a piezoelectric spring, and a light head mass. Miniaturized tonpilz transducers are potentially interesting for the 10 to 100 MHz frequency range in imaging transducers due to their high efficiency and output capabilities. Piezoelectric thin films can be used as the active element in the construction of miniaturized tonpilz structures. A 4-10 μm film is necessary for the mass-spring-mass system to resonate at these high frequencies. In this work, fabrication and characterization of lead zirconate titanate (PZT) thick films on conductive oxide LaNiO3 (LNO) coated silicon on insulator (SOI) substrates will be reported for this application. First, conductive LNO thin films, approximately 300 nm in thickness, were grown on SOI substrates by a metal-organic decomposition (MOD) method. The room temperature resistivity of the LNO was 6.5 × 10-4 Ω·cm. Randomly oriented PZT (52/48) films up to 7 μm thick were then deposited using a sol-gel process on the LNO coated SOI substrates. 20 mol.% excess lead was added to the solutions to compensate for lead volatilization during film heat treatments. PZT films with LNO bottom electrodes showed good dielectric and ferroelectric properties. The dielectric permittivity (at 1 kHz) was over 1000. The remanent polarization of PZT films was larger than 26 μC/cm2. The e31,f coefficient of PZT thick films was larger than -6.5 C/m2 when poled at -75 kV/cm for 15 minutes. A silver layer approximately 40 μm thick was screen-printed onto the PZT film to form the tail mass of the tonpilz structure. Elements were diced and the bulk silicon was removed by dry and wet-etching methods to leave the p-type silicon layer as tonpilz head mass. Fabrication of MEMS tonpilz microstructures will also be presented.

Original languageEnglish (US)
Pages (from-to)161-166
Number of pages6
JournalMaterials Research Society Symposium - Proceedings
Volume687
StatePublished - Jan 1 2002
EventMaterials Science of Microelectromechanical Systems (MEMS) Devices IV - Boston, MA, United States
Duration: Nov 25 2001Nov 28 2001

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Fabrication of MEMS tonpilz transducers'. Together they form a unique fingerprint.

Cite this