Friction and Tribochemical Wear Behaviors of Native Oxide Layer on Silicon at Nanoscale

Lei Chen, Chen Xiao, Xin He, Bingjun Yu, Seong H. Kim, Linmao Qian

Research output: Contribution to journalArticlepeer-review

17 Scopus citations

Abstract

The friction and tribochemical wear of native oxide (SiOx) layers formed on a silicon surface were investigated with atomic force microscopy using a silica (SiO2) sphere tip in ambient air (50% relative humidity). The native SiOx layer thickness was determined to be ~0.8 nm with auger electron spectroscopy. The oxide-free Si/H terminated silicon surface was also studied as a reference for comparison. It was found that friction is higher on the Si/SiOx surface than the Si/H surface; but, the wear of the Si/H surface occurs much more readily than that of the Si/SiOx surface when wear depth is less than the thickness of native oxide layer on Si/SiOx surface (~0.8 nm). Based on attenuated total reflection infrared spectroscopy analysis, the friction appears to be governed by the thickness and structure of the adsorbed water layer. Although the wear process in humid conditions is through tribochemical reactions involving the adsorbed water, the removal rate of the substrate layer varies depending on the effective activation energy. These findings are important for the tribological design of silicon-based micro/nanodevices working in humid ambience.

Original languageEnglish (US)
Article number139
JournalTribology Letters
Volume65
Issue number4
DOIs
StatePublished - Dec 2017

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

Fingerprint Dive into the research topics of 'Friction and Tribochemical Wear Behaviors of Native Oxide Layer on Silicon at Nanoscale'. Together they form a unique fingerprint.

Cite this