Growth and luminescence mechanisms of Ba2ErCl7: a new laser up-conversion crystal

Guangyong Zhou, Jianru Han, Shujun Zhang, Zhenxiang Cheng, Huanchu Chen

Research output: Contribution to journalArticle

Abstract

A modified synthesis method for the preparation of Ba2ErCl7, a new laser up-conversion material using Er2O3, BaCl2·2H2O and NH4Cl, is reported for the first time. Single crystals 5-8 mm in diameter and 10-20 mm in length were grown by both the Czochralski and Bridgman methods. The transmittance spectra for a Ba2ErCl7 single crystal was first measured using a HITACHI U-3500 spectrophotometer. There were three intense absorption peaks 4I9/2, 4I11/2 and 4I13/2 in the infrared range which can be excited by 803 and 980 nm and 1.5 μm laser diode (LD), respectively. The cut-off wavelength of the crystal was 230 nm. Intense green luminescence was observed when the crystals were pumped by an 803 nm LD. Up-conversion mechanisms are discussed.

Original languageEnglish (US)
Pages (from-to)699-703
Number of pages5
JournalJournal of Crystal Growth
Volume210
Issue number4
DOIs
StatePublished - Mar 2000

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Inorganic Chemistry
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Growth and luminescence mechanisms of Ba<sub>2</sub>ErCl<sub>7</sub>: a new laser up-conversion crystal'. Together they form a unique fingerprint.

  • Cite this