High temperature (NaBi) 0.480.04Bi 2Nb 2O 9-based piezoelectric ceramics

Zhi Gang Gai, Jin Feng Wang, Ming Lei Zhao, Chun Ming Wang, Guo Zhong Zang, Bao Quan Ming, Peng Qi, Shujun Zhang, Thomas R. Shrout

Research output: Contribution to journalArticle

62 Scopus citations

Abstract

The effect of (LiCe) substitution for A site on the properties of (NaBi) 0.480.04 Bi 2Nb 2O 9 (NB□N)-based ceramics was investigated. The coercive fields (E C) of NB□N)-based ceramics were significantly decreased from 61.0 to 32.5 kV/cm and the Curie temperature (T C) gradually decreases from 820 to 803°C with increasing the (LiCe) modification. The piezoelectric coefficient d 33, planar coupling factor k p, and mechanical quality factor Q of (NaBi) 0.38(LiCe) 0.050.14Bi 2Nb 2O 9 ceramic were found to be 27 pC/N, 11.2%, and 2600, respectively, together with the high T C (∼809°C) and stable piezoelectric properties, demonstrating that the (LiCe) modified NB□N-based material a promising candidate for high temperature applications.

Original languageEnglish (US)
Article number012907
JournalApplied Physics Letters
Volume89
Issue number1
DOIs
StatePublished - Jul 14 2006

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy (miscellaneous)

Fingerprint Dive into the research topics of 'High temperature (NaBi) <sub>0.48</sub>□ <sub>0.04</sub>Bi <sub>2</sub>Nb <sub>2</sub>O <sub>9</sub>-based piezoelectric ceramics'. Together they form a unique fingerprint.

  • Cite this

    Gai, Z. G., Wang, J. F., Zhao, M. L., Wang, C. M., Zang, G. Z., Ming, B. Q., Qi, P., Zhang, S., & Shrout, T. R. (2006). High temperature (NaBi) 0.480.04Bi 2Nb 2O 9-based piezoelectric ceramics. Applied Physics Letters, 89(1), [012907]. https://doi.org/10.1063/1.2216355