Impact of chemical composition on precipitate morphology in an additively manufactured nickel base superalloy

J. S. Zuback, P. Moradifar, Z. Khayat, Nasim Alem, Todd Palmer

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

Changes in the iron content within the allowable composition range in Inconel® 625 produce significant differences in the grain size and mechanical properties during laser-based directed energy deposition additive manufacturing. The resulting precipitate types and morphologies, which contribute to these different properties, originate from a complex interplay between iron, silicon, and titanium. While the addition of iron has traditionally been shown to promote Laves phase formation, thermodynamic calculations have shown that silicon contents in excess of 0.05 wt% are also required to promote its formation. For example, relatively low iron (1 wt%), low titanium (0.019 wt%), and high silicon (0.37 wt%) contents led to the formation of Laves phase. On the other hand, high iron (4 wt%), high titanium (0.19 wt%), and low silicon (0.035 wt%) contents produce MN nitrides and no Laves phase. By increasing the titanium concentration, the precipitation of nitrides rich in titanium and niobium is promoted in the liquid, and Laves phase formation is suppressed during solidification. After hot isostatic pressing, the precipitate distribution displayed minimal differences with that found in the as-deposited condition for both material chemistries. However, the precipitates in the as-deposited low iron material grew larger and developed a blocky morphology while the original Laves phase partially transformed to M2N nitrides rich in Nb, Cr, and Mo. In the high iron material, the MN nitrides became depleted in niobium and further enriched in titanium while maintaining a size similar to those in the as-deposited condition.

Original languageEnglish (US)
Pages (from-to)446-457
Number of pages12
JournalJournal of Alloys and Compounds
Volume798
DOIs
StatePublished - Aug 25 2019

Fingerprint

Titanium
Nickel
Superalloys
Precipitates
Iron
Nitrides
Silicon
Chemical analysis
Niobium
3D printers
Silicon steel
Hot isostatic pressing
Solidification
Thermodynamics
Mechanical properties
Lasers
Liquids

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this

@article{09d702d9e296476a86ad5249413df588,
title = "Impact of chemical composition on precipitate morphology in an additively manufactured nickel base superalloy",
abstract = "Changes in the iron content within the allowable composition range in Inconel{\circledR} 625 produce significant differences in the grain size and mechanical properties during laser-based directed energy deposition additive manufacturing. The resulting precipitate types and morphologies, which contribute to these different properties, originate from a complex interplay between iron, silicon, and titanium. While the addition of iron has traditionally been shown to promote Laves phase formation, thermodynamic calculations have shown that silicon contents in excess of 0.05 wt{\%} are also required to promote its formation. For example, relatively low iron (1 wt{\%}), low titanium (0.019 wt{\%}), and high silicon (0.37 wt{\%}) contents led to the formation of Laves phase. On the other hand, high iron (4 wt{\%}), high titanium (0.19 wt{\%}), and low silicon (0.035 wt{\%}) contents produce MN nitrides and no Laves phase. By increasing the titanium concentration, the precipitation of nitrides rich in titanium and niobium is promoted in the liquid, and Laves phase formation is suppressed during solidification. After hot isostatic pressing, the precipitate distribution displayed minimal differences with that found in the as-deposited condition for both material chemistries. However, the precipitates in the as-deposited low iron material grew larger and developed a blocky morphology while the original Laves phase partially transformed to M2N nitrides rich in Nb, Cr, and Mo. In the high iron material, the MN nitrides became depleted in niobium and further enriched in titanium while maintaining a size similar to those in the as-deposited condition.",
author = "Zuback, {J. S.} and P. Moradifar and Z. Khayat and Nasim Alem and Todd Palmer",
year = "2019",
month = "8",
day = "25",
doi = "10.1016/j.jallcom.2019.05.230",
language = "English (US)",
volume = "798",
pages = "446--457",
journal = "Journal of Alloys and Compounds",
issn = "0925-8388",
publisher = "Elsevier BV",

}

Impact of chemical composition on precipitate morphology in an additively manufactured nickel base superalloy. / Zuback, J. S.; Moradifar, P.; Khayat, Z.; Alem, Nasim; Palmer, Todd.

In: Journal of Alloys and Compounds, Vol. 798, 25.08.2019, p. 446-457.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Impact of chemical composition on precipitate morphology in an additively manufactured nickel base superalloy

AU - Zuback, J. S.

AU - Moradifar, P.

AU - Khayat, Z.

AU - Alem, Nasim

AU - Palmer, Todd

PY - 2019/8/25

Y1 - 2019/8/25

N2 - Changes in the iron content within the allowable composition range in Inconel® 625 produce significant differences in the grain size and mechanical properties during laser-based directed energy deposition additive manufacturing. The resulting precipitate types and morphologies, which contribute to these different properties, originate from a complex interplay between iron, silicon, and titanium. While the addition of iron has traditionally been shown to promote Laves phase formation, thermodynamic calculations have shown that silicon contents in excess of 0.05 wt% are also required to promote its formation. For example, relatively low iron (1 wt%), low titanium (0.019 wt%), and high silicon (0.37 wt%) contents led to the formation of Laves phase. On the other hand, high iron (4 wt%), high titanium (0.19 wt%), and low silicon (0.035 wt%) contents produce MN nitrides and no Laves phase. By increasing the titanium concentration, the precipitation of nitrides rich in titanium and niobium is promoted in the liquid, and Laves phase formation is suppressed during solidification. After hot isostatic pressing, the precipitate distribution displayed minimal differences with that found in the as-deposited condition for both material chemistries. However, the precipitates in the as-deposited low iron material grew larger and developed a blocky morphology while the original Laves phase partially transformed to M2N nitrides rich in Nb, Cr, and Mo. In the high iron material, the MN nitrides became depleted in niobium and further enriched in titanium while maintaining a size similar to those in the as-deposited condition.

AB - Changes in the iron content within the allowable composition range in Inconel® 625 produce significant differences in the grain size and mechanical properties during laser-based directed energy deposition additive manufacturing. The resulting precipitate types and morphologies, which contribute to these different properties, originate from a complex interplay between iron, silicon, and titanium. While the addition of iron has traditionally been shown to promote Laves phase formation, thermodynamic calculations have shown that silicon contents in excess of 0.05 wt% are also required to promote its formation. For example, relatively low iron (1 wt%), low titanium (0.019 wt%), and high silicon (0.37 wt%) contents led to the formation of Laves phase. On the other hand, high iron (4 wt%), high titanium (0.19 wt%), and low silicon (0.035 wt%) contents produce MN nitrides and no Laves phase. By increasing the titanium concentration, the precipitation of nitrides rich in titanium and niobium is promoted in the liquid, and Laves phase formation is suppressed during solidification. After hot isostatic pressing, the precipitate distribution displayed minimal differences with that found in the as-deposited condition for both material chemistries. However, the precipitates in the as-deposited low iron material grew larger and developed a blocky morphology while the original Laves phase partially transformed to M2N nitrides rich in Nb, Cr, and Mo. In the high iron material, the MN nitrides became depleted in niobium and further enriched in titanium while maintaining a size similar to those in the as-deposited condition.

UR - http://www.scopus.com/inward/record.url?scp=85066866049&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85066866049&partnerID=8YFLogxK

U2 - 10.1016/j.jallcom.2019.05.230

DO - 10.1016/j.jallcom.2019.05.230

M3 - Article

AN - SCOPUS:85066866049

VL - 798

SP - 446

EP - 457

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

SN - 0925-8388

ER -