Magnetorheology of submicron diameter iron microwires dispersed in silicone oil

R. C. Bell, J. O. Karli, A. N. Vavreck, D. T. Zimmerman, G. T. Ngatu, N. M. Wereley

Research output: Contribution to journalArticle

112 Scopus citations

Abstract

We investigate the magnetorheological (MR) properties of suspensions containing iron microwires with 260nm diameter and two distinct length distributions of 5.4 5.2νm and 7.6 5.1νm suspended in silicone oil (0.45Pas). The rheological properties of these fluids were determined using a parallel plate rheometer equipped with a variable strength electromagnet. The shear stress was measured as a function of shear rate for increasing applied magnetic fields. These results were modeled using the Bingham-plastic constitutive model to determine the apparent yield stress and viscosity as a function of increasing volume fraction and length of microwires. At a saturated magnetic flux density, the yield stress using the 5.4νm microwires was found to be 0.65, 2.23, and 4.76 kPa for the 2, 4, and 6vol% suspensions, respectively. For the 7.6νm wires, the yield stress increases to 8.2 kPa for the 6vol% suspension. Compared with conventional MR fluids employing spherical particles, the degree of settling is markedly decreased in the microwire-based fluids. At 6vol%, conventional fluids display appreciable settling whereas the microwire-based fluids display no discernable settling. Moreover, the rod-shaped microwires are shown to increase the yield stress of the fluids and enhance the MR performance.

Original languageEnglish (US)
Article number015028
JournalSmart Materials and Structures
Volume17
Issue number1
DOIs
StatePublished - Feb 1 2008

All Science Journal Classification (ASJC) codes

  • Signal Processing
  • Civil and Structural Engineering
  • Atomic and Molecular Physics, and Optics
  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Magnetorheology of submicron diameter iron microwires dispersed in silicone oil'. Together they form a unique fingerprint.

  • Cite this