Mist deposition of micron-thick lead zirconate titanate films

Research output: Contribution to journalArticle

3 Citations (Scopus)

Abstract

A majority of the work published on liquid source misted chemical deposition (LSMCD) has focused on the fabrication of thin ferroelectric films for random access memory (RAM) applications. However, the ability of LSMCD to combine the characteristically good stoichiometry control of a chemical solution deposition process with good film conformality, makes this a desirable technique for other applications, including microactuators and integrated passive components. For these applications, though, LSMCD is limited by its low throughput. This paper describes the feasibility of depositing micron-thick lead zirconate titanate (PZT) films using the LSMCD tool. PZT films of 52/48 composition were deposited on both platinized silicon and platinized alumina substrates. The chamber temperature and the delivery geometry of the LSMCD tool were identified as limiting factors in the rate at which micron-thick samples can be prepared. By switching to a focused nozzle delivery geometry and increasing the chamber temperature from room temperature to 60°C, the total process time for 1 μm thick films can be reduced from 480 min to 90 min. Polarization hysteresis measurements indicated a 75% higher remanent polarization for PZT films deposited on platinized alumina substrates (35 μC/cm2) compared to those deposed on platinized silicon substrates (20 μC/cm2). The polarization loop for the silicon substrate sample was also tilted. These observations are evidence of higher tensile stresses in the PZT films deposited on silicon substrates due to a larger mismatch in the thermal expansion coefficients of the film and the substrate.

Original languageEnglish (US)
Pages (from-to)553-558
Number of pages6
JournalMaterials Research Society Symposium - Proceedings
Volume784
StatePublished - Jan 1 2003

Fingerprint

mist
Fog
Silicon
Substrates
Liquids
Aluminum Oxide
liquids
silicon
Alumina
delivery
Polarization
polarization
aluminum oxides
chambers
Microactuators
Ferroelectric thin films
Geometry
Remanence
Thick films
Tensile stress

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

@article{f24d1bed079746649d61a2c0602fa295,
title = "Mist deposition of micron-thick lead zirconate titanate films",
abstract = "A majority of the work published on liquid source misted chemical deposition (LSMCD) has focused on the fabrication of thin ferroelectric films for random access memory (RAM) applications. However, the ability of LSMCD to combine the characteristically good stoichiometry control of a chemical solution deposition process with good film conformality, makes this a desirable technique for other applications, including microactuators and integrated passive components. For these applications, though, LSMCD is limited by its low throughput. This paper describes the feasibility of depositing micron-thick lead zirconate titanate (PZT) films using the LSMCD tool. PZT films of 52/48 composition were deposited on both platinized silicon and platinized alumina substrates. The chamber temperature and the delivery geometry of the LSMCD tool were identified as limiting factors in the rate at which micron-thick samples can be prepared. By switching to a focused nozzle delivery geometry and increasing the chamber temperature from room temperature to 60°C, the total process time for 1 μm thick films can be reduced from 480 min to 90 min. Polarization hysteresis measurements indicated a 75{\%} higher remanent polarization for PZT films deposited on platinized alumina substrates (35 μC/cm2) compared to those deposed on platinized silicon substrates (20 μC/cm2). The polarization loop for the silicon substrate sample was also tilted. These observations are evidence of higher tensile stresses in the PZT films deposited on silicon substrates due to a larger mismatch in the thermal expansion coefficients of the film and the substrate.",
author = "Losego, {Mark D.} and Trolier-McKinstry, {Susan E.}",
year = "2003",
month = "1",
day = "1",
language = "English (US)",
volume = "784",
pages = "553--558",
journal = "Materials Research Society Symposium - Proceedings",
issn = "0272-9172",
publisher = "Materials Research Society",

}

Mist deposition of micron-thick lead zirconate titanate films. / Losego, Mark D.; Trolier-McKinstry, Susan E.

In: Materials Research Society Symposium - Proceedings, Vol. 784, 01.01.2003, p. 553-558.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Mist deposition of micron-thick lead zirconate titanate films

AU - Losego, Mark D.

AU - Trolier-McKinstry, Susan E.

PY - 2003/1/1

Y1 - 2003/1/1

N2 - A majority of the work published on liquid source misted chemical deposition (LSMCD) has focused on the fabrication of thin ferroelectric films for random access memory (RAM) applications. However, the ability of LSMCD to combine the characteristically good stoichiometry control of a chemical solution deposition process with good film conformality, makes this a desirable technique for other applications, including microactuators and integrated passive components. For these applications, though, LSMCD is limited by its low throughput. This paper describes the feasibility of depositing micron-thick lead zirconate titanate (PZT) films using the LSMCD tool. PZT films of 52/48 composition were deposited on both platinized silicon and platinized alumina substrates. The chamber temperature and the delivery geometry of the LSMCD tool were identified as limiting factors in the rate at which micron-thick samples can be prepared. By switching to a focused nozzle delivery geometry and increasing the chamber temperature from room temperature to 60°C, the total process time for 1 μm thick films can be reduced from 480 min to 90 min. Polarization hysteresis measurements indicated a 75% higher remanent polarization for PZT films deposited on platinized alumina substrates (35 μC/cm2) compared to those deposed on platinized silicon substrates (20 μC/cm2). The polarization loop for the silicon substrate sample was also tilted. These observations are evidence of higher tensile stresses in the PZT films deposited on silicon substrates due to a larger mismatch in the thermal expansion coefficients of the film and the substrate.

AB - A majority of the work published on liquid source misted chemical deposition (LSMCD) has focused on the fabrication of thin ferroelectric films for random access memory (RAM) applications. However, the ability of LSMCD to combine the characteristically good stoichiometry control of a chemical solution deposition process with good film conformality, makes this a desirable technique for other applications, including microactuators and integrated passive components. For these applications, though, LSMCD is limited by its low throughput. This paper describes the feasibility of depositing micron-thick lead zirconate titanate (PZT) films using the LSMCD tool. PZT films of 52/48 composition were deposited on both platinized silicon and platinized alumina substrates. The chamber temperature and the delivery geometry of the LSMCD tool were identified as limiting factors in the rate at which micron-thick samples can be prepared. By switching to a focused nozzle delivery geometry and increasing the chamber temperature from room temperature to 60°C, the total process time for 1 μm thick films can be reduced from 480 min to 90 min. Polarization hysteresis measurements indicated a 75% higher remanent polarization for PZT films deposited on platinized alumina substrates (35 μC/cm2) compared to those deposed on platinized silicon substrates (20 μC/cm2). The polarization loop for the silicon substrate sample was also tilted. These observations are evidence of higher tensile stresses in the PZT films deposited on silicon substrates due to a larger mismatch in the thermal expansion coefficients of the film and the substrate.

UR - http://www.scopus.com/inward/record.url?scp=2942631364&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=2942631364&partnerID=8YFLogxK

M3 - Article

VL - 784

SP - 553

EP - 558

JO - Materials Research Society Symposium - Proceedings

JF - Materials Research Society Symposium - Proceedings

SN - 0272-9172

ER -