Particle size effects on yttrium aluminum garnet (YAG) phase formation by solid-state reaction

Elizabeth R. Kupp, Sujarinee Kochawattana, Sang Ho Lee, Scott Misture, Gary L. Messing

Research output: Contribution to journalArticle

15 Scopus citations

Abstract

The solid-state reaction of yttrium aluminum garnet (YAG, Y3Al5O12) during the heat treatment of Y2O3 and Al2O3 powder mixtures, differing in particle size and size ratio, was quantified using in situ high-temperature x-ray analysis and Rietveld refinement. Y2O3 particle size has the most profound effect on YAG formation. When the Y2O3 particle size was decreased from 5000 to 30 nm (on reaction with 270 nm Al2O3), the YAG formation rate increased from 20 to 48 vol% min-1 over the temperature range of 1350-1450 °C. In this case, the final YAG content increased from 75 to 91 vol%. A simple model that includes the reactant particle coordination number, and thus particle size ratio, shows that when the size ratio (dA/dY) is >1 diffusion through the alumina powder is rate controlling whereas when the ratio is <1, diffusion through the yttria, intermediate phases, and YAG is rate controlling.

Original languageEnglish (US)
Pages (from-to)2303-2311
Number of pages9
JournalJournal of Materials Research
Volume29
Issue number19
DOIs
StatePublished - Jul 28 2014

    Fingerprint

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Cite this