Residual ferroelectricity in barium strontium titanate thin film tunable dielectrics

L. M. Garten, P. Lam, D. Harris, J. P. Maria, S. Trolier-Mckinstry

Research output: Contribution to journalArticle

33 Scopus citations

Abstract

Loss reduction is critical to develop Ba1-xSr xTiO3 thin film tunable microwave dielectric components and dielectric energy storage devices. The presence of ferroelectricity, and hence the domain wall contributions to dielectric loss, will degrade the tunable performance in the microwave region. In this work, residual ferroelectricity - a persistent ferroelectric response above the global phase transition temperature - was characterized in tunable dielectrics using Rayleigh analysis. Chemical solution deposited Ba0.7Sr0.3TiO3 films, with relative tunabilities of 86% over 250 kV/cm at 100 kHz, demonstrated residual ferroelectricity 65 °C above the ostensible paraelectric transition temperature. Frequency dispersion observed in the dielectric temperature response was consistent with the presence of nanopolar regions as one source of residual ferroelectricity. The application of AC electric field for the Rayleigh analysis of these samples led to a doubling of the dielectric loss for fields over 10 kV/cm at room temperature.

Original languageEnglish (US)
Article number044104
JournalJournal of Applied Physics
Volume116
Issue number4
DOIs
StatePublished - Jul 28 2014

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Residual ferroelectricity in barium strontium titanate thin film tunable dielectrics'. Together they form a unique fingerprint.

  • Cite this