In this paper, a vertical-aligned silicon nanowires (Si NWs) array has been synthesized and implemented to the Si NW-array-textured solar cells for photovoltaic application. The optical properties of a Si NWs array on both the plane and pyramid-array-textured substrates were examined in terms of optical reflection property. Less than 2% reflection ratio at 800 nm wavelength was achieved. Using leftover monocrystalline Si (c-Si) wafer (125×125 mm 2), a 16.5% energy conversion efficiency, with 35.4% enhancement compared to the pyramid-array-textured c-Si solar cells, was made by the Si NW-array-textured solar cells due to their enhanced optical absorption characteristics. However, without SiNx passivation, the short circuit current reduced due to the increased surface recombination when using Si NWs array as surface texturing, indicating that an optimum surface passivation was prerequisite in high-efficiency Si NW-array-textured solar cells.
|Original language||English (US)|
|Journal||Journal of Applied Physics|
|State||Published - Nov 1 2010|
All Science Journal Classification (ASJC) codes
- Physics and Astronomy(all)