Sintering of the ultrahigh pressure densified hydroxyapatite monolithic xerogels

Ján Majling, Peter Znáik, Angela Palová, Stefan Svetík, Stefan Kovalík, Dinesh K. Agrawal, Rustum Roy

Research output: Contribution to journalArticlepeer-review

18 Scopus citations

Abstract

Dense and translucent ceramics were prepared by sintering of cylindrical preforms of hydroxyapatite extruded from xerogels. Extruded specimens were dried as monoliths and then consolidated by applying cold isostatic pressure, ranging from 500 to 1500 MPa. Upon heating the samples began to densify at 610 °C, and the densification/sintering was completed at 870 °C as was evidenced by the dilatometry plot indicating no further shrinkage. The sintered specimens thus formed were translucent in appearance. Further heating of the samples up to 1200 °C resulted in their "bloating" or creation of pores in the originally dense matrix. Pore creation within the structure is reproducible, it proceeds from the surface to the interior of the sample, and its spreading can be thermally controlled. Pore evolution within the single phase dense polycrystalline material is not related to the frequently occurring phenomenon of microcracking in ceramics during cooling.

Original languageEnglish (US)
Pages (from-to)198-202
Number of pages5
JournalJournal of Materials Research
Volume12
Issue number1
DOIs
StatePublished - 1997

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Sintering of the ultrahigh pressure densified hydroxyapatite monolithic xerogels'. Together they form a unique fingerprint.

Cite this