Structure and microwave dielectric properties of Ca1-xYxTi1-xAlxO3 (CYTA) ceramics

Antonio Feteira, Derek C. Sinclair, Michael T. Lanagan

Research output: Contribution to journalArticle

40 Scopus citations

Abstract

The structure and dielectric properties of Ca1-xYx Ti1-xAlxO3 (CYTA) ceramics prepared by the mixed-oxide route have been investigated. CYTA forms a complete solid solution with an orthorhombic perovskite structure. Residual Y4Al2O2 and Y3Al5O12 resulting from incomplete reaction are observed for ≥ 0.9. Scanning electron microscopy shows that CYTA ceramics exhibit uniform microstructures, with an average grain size that decreases from ∼200 μm at x = 0 to ∼10 μm at x = 1.0. Transmission electron microscopy of CYTA (x = 0.3) ceramics reveals the presence of ferroelastic domains, and electron-diffraction patterns are indexed on the Pnma space group, consistent with an a+b-b- octahedral tilted structure. The relative permittivity, εr, decreases continuously from 170 to 12, while the microwave quality factor, Q·fr increases from 10,000 to 12,000 GHz, for x = 0 and 1, respectively. CYTA (x = ceramics exhibit εr ∼ 38, Q·fr of ∼14,212 GHz, and a temperature coefficient of resonance frequency, τf, of -14 ppm/°C. Small additions of acceptor (0.3 wt% ZnO) or donor (1 wt% Nb2O5) dopants decrease Q·fr by ∼20-30%, respectively. 0.30).

Original languageEnglish (US)
Pages (from-to)2391-2399
Number of pages9
JournalJournal of Materials Research
Volume20
Issue number9
DOIs
StatePublished - Sep 1 2005

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Structure and microwave dielectric properties of Ca<sub>1-x</sub>Y<sub>x</sub>Ti<sub>1-x</sub>Al<sub>x</sub>O<sub>3</sub> (CYTA) ceramics'. Together they form a unique fingerprint.

  • Cite this