The effect of point defects on the dissolution of zinc oxide in sodium hydroxide solutions

G. Rogers, G. Simkovich, Kwadwo Asare Osseo-Asare

Research output: Contribution to journalArticle

5 Citations (Scopus)

Abstract

The dissolution behavior of sintered zinc oxide in aqueous solutions of NaOH has been studied as a function of varying concentrations of lithia, alumina, and chromia as solid state dopants. Both the pure and doped zinc oxide samples were found to obey the shrinking particle model of dissolution, and there was a lack of dependence of the dissolution rate on agitation speed. An activation energy of 48.1 kJ/mol (11.5 kcal/mol) was obtained for the undoped ZnO material. It is proposed that the desorption of surface hydroxyl complexes constitutes the rate controlling step. Additions of up to 1.0 mol percent Cr2,O3 and Al2O3 decreased the dissolution rate. An opposite effect was observed for the addition of Li2O. Dopant-induced changes in zinc oxide surface chemistry have been used to interpret the observed difference in the effects of the higher-valent and lower-valent dopants. Zinc oxide is an n-type semiconductor with an equivalent amount of zinc interstitials and quasi-free electrons. Doping with alumina and chromia results in an increase in negatively charged point defects (quasi-free electrons), reducing adsorption of OH- species on the zinc oxide surface and thereby decreasing dissolution. Doping with lithia increases the concentration of positively charged point defects (zinc interstitials), thus facilitating surface hydroxylation and dissolution.

Original languageEnglish (US)
Pages (from-to)313-328
Number of pages16
JournalHydrometallurgy
Volume10
Issue number3
DOIs
StatePublished - Jan 1 1983

Fingerprint

Zinc Oxide
Sodium Hydroxide
Point defects
Zinc oxide
Dissolution
Sodium
Doping (additives)
Aluminum Oxide
Zinc
Alumina
Hydroxylation
Electrons
Surface chemistry
Hydroxyl Radical
Desorption
Activation energy
Semiconductor materials
Adsorption

All Science Journal Classification (ASJC) codes

  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Cite this

@article{db7963ec070c490b8855df9363dd0c69,
title = "The effect of point defects on the dissolution of zinc oxide in sodium hydroxide solutions",
abstract = "The dissolution behavior of sintered zinc oxide in aqueous solutions of NaOH has been studied as a function of varying concentrations of lithia, alumina, and chromia as solid state dopants. Both the pure and doped zinc oxide samples were found to obey the shrinking particle model of dissolution, and there was a lack of dependence of the dissolution rate on agitation speed. An activation energy of 48.1 kJ/mol (11.5 kcal/mol) was obtained for the undoped ZnO material. It is proposed that the desorption of surface hydroxyl complexes constitutes the rate controlling step. Additions of up to 1.0 mol percent Cr2,O3 and Al2O3 decreased the dissolution rate. An opposite effect was observed for the addition of Li2O. Dopant-induced changes in zinc oxide surface chemistry have been used to interpret the observed difference in the effects of the higher-valent and lower-valent dopants. Zinc oxide is an n-type semiconductor with an equivalent amount of zinc interstitials and quasi-free electrons. Doping with alumina and chromia results in an increase in negatively charged point defects (quasi-free electrons), reducing adsorption of OH- species on the zinc oxide surface and thereby decreasing dissolution. Doping with lithia increases the concentration of positively charged point defects (zinc interstitials), thus facilitating surface hydroxylation and dissolution.",
author = "G. Rogers and G. Simkovich and Osseo-Asare, {Kwadwo Asare}",
year = "1983",
month = "1",
day = "1",
doi = "10.1016/0304-386X(83)90062-2",
language = "English (US)",
volume = "10",
pages = "313--328",
journal = "Hydrometallurgy",
issn = "0304-386X",
publisher = "Elsevier",
number = "3",

}

The effect of point defects on the dissolution of zinc oxide in sodium hydroxide solutions. / Rogers, G.; Simkovich, G.; Osseo-Asare, Kwadwo Asare.

In: Hydrometallurgy, Vol. 10, No. 3, 01.01.1983, p. 313-328.

Research output: Contribution to journalArticle

TY - JOUR

T1 - The effect of point defects on the dissolution of zinc oxide in sodium hydroxide solutions

AU - Rogers, G.

AU - Simkovich, G.

AU - Osseo-Asare, Kwadwo Asare

PY - 1983/1/1

Y1 - 1983/1/1

N2 - The dissolution behavior of sintered zinc oxide in aqueous solutions of NaOH has been studied as a function of varying concentrations of lithia, alumina, and chromia as solid state dopants. Both the pure and doped zinc oxide samples were found to obey the shrinking particle model of dissolution, and there was a lack of dependence of the dissolution rate on agitation speed. An activation energy of 48.1 kJ/mol (11.5 kcal/mol) was obtained for the undoped ZnO material. It is proposed that the desorption of surface hydroxyl complexes constitutes the rate controlling step. Additions of up to 1.0 mol percent Cr2,O3 and Al2O3 decreased the dissolution rate. An opposite effect was observed for the addition of Li2O. Dopant-induced changes in zinc oxide surface chemistry have been used to interpret the observed difference in the effects of the higher-valent and lower-valent dopants. Zinc oxide is an n-type semiconductor with an equivalent amount of zinc interstitials and quasi-free electrons. Doping with alumina and chromia results in an increase in negatively charged point defects (quasi-free electrons), reducing adsorption of OH- species on the zinc oxide surface and thereby decreasing dissolution. Doping with lithia increases the concentration of positively charged point defects (zinc interstitials), thus facilitating surface hydroxylation and dissolution.

AB - The dissolution behavior of sintered zinc oxide in aqueous solutions of NaOH has been studied as a function of varying concentrations of lithia, alumina, and chromia as solid state dopants. Both the pure and doped zinc oxide samples were found to obey the shrinking particle model of dissolution, and there was a lack of dependence of the dissolution rate on agitation speed. An activation energy of 48.1 kJ/mol (11.5 kcal/mol) was obtained for the undoped ZnO material. It is proposed that the desorption of surface hydroxyl complexes constitutes the rate controlling step. Additions of up to 1.0 mol percent Cr2,O3 and Al2O3 decreased the dissolution rate. An opposite effect was observed for the addition of Li2O. Dopant-induced changes in zinc oxide surface chemistry have been used to interpret the observed difference in the effects of the higher-valent and lower-valent dopants. Zinc oxide is an n-type semiconductor with an equivalent amount of zinc interstitials and quasi-free electrons. Doping with alumina and chromia results in an increase in negatively charged point defects (quasi-free electrons), reducing adsorption of OH- species on the zinc oxide surface and thereby decreasing dissolution. Doping with lithia increases the concentration of positively charged point defects (zinc interstitials), thus facilitating surface hydroxylation and dissolution.

UR - http://www.scopus.com/inward/record.url?scp=0020764721&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0020764721&partnerID=8YFLogxK

U2 - 10.1016/0304-386X(83)90062-2

DO - 10.1016/0304-386X(83)90062-2

M3 - Article

AN - SCOPUS:0020764721

VL - 10

SP - 313

EP - 328

JO - Hydrometallurgy

JF - Hydrometallurgy

SN - 0304-386X

IS - 3

ER -