The significance of in situ conditions in the characterization of GaSb nanopatterned surfaces via ion beam sputtering

Osman El-Atwani, J. P. Allain, Alex Cimaroli, Sami Ortoleva

Research output: Contribution to journalArticlepeer-review

21 Scopus citations

Abstract

A systematic study is conducted in order to elucidate the underlying mechanism(s) for nanopatterning with low-energy irradiation of GaSb (100) under normal incidence. Ion energies between 50 and 1000 eV of Ar and ion fluences of up to 1018cm-2 were employed. Characterization of the shallow (e.g., 1 to 6 nm) amorphous phase region induced by irradiation and the sub-surface crystalline phase region is accomplished with low-energy ion scattering spectroscopy and x-ray photoelectron spectroscopy, respectively. In situ studies are conducted due to the strong chemical affinity for oxygen of GaSb. The studies conclude that at energies below 200 eV, the native oxide layer hampers nanopatterning until it becomes removed at a fluence of approximately 5 1016cm-2. At this energy and threshold fluence, the surface is enriched with Ga atoms during irradiation. At energies above 200 eV, the native oxide layer is efficiently removed in the early irradiation stages, and thus the detrimental effects from the oxide on nanopatterning are negligible. In situ surface concentration quantification indicates that the surface enrichment with Sb atoms in the amorphous phase layer increases with the incident ion energy. Post-air exposure characterization reveals that the measured enrichment of the surface with gallium is due to oxygen reduction by Ga atoms segregated from both the amorphous and the crystalline phase regions as a result of air exposure.

Original languageEnglish (US)
Article number074301
JournalJournal of Applied Physics
Volume110
Issue number7
DOIs
StatePublished - Oct 1 2011

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'The significance of in situ conditions in the characterization of GaSb nanopatterned surfaces via ion beam sputtering'. Together they form a unique fingerprint.

Cite this