Unusual water vapor adsorption behavior of montmorillonite pillared with ceramic oxides

P. Malla, S. Yamanaka, Sridhar Komarneni

Research output: Contribution to journalArticle

47 Citations (Scopus)

Abstract

A montmorillonite was pillared with oxide pillars such as Al2O3, ZrO2 and TiO2 to generate permanent microporosity in the interlayers. The X-ray powder diffraction analysis and nitrogen and water adsorption measurements indicated that the pillars were stable at least up to 600°C. The slit widths (pore size) are on the order of 7-9 Å for Al2O3, 8-10 Å for ZrO2 and 14-17 Å for TiO2 pillared clay. The TiO2 pillared clay exhibited Brunauer type IV isotherm that fits BET linear equation for both nitrogen and water. Although Al2O3 and ZrO2 pillared clays followed Brunauer type I isotherm with nitrogen, their water adsorption isotherms exhibited unusual shapes and did not fit either Langmuir or BET equation. The unique pore sizes of these pillared clays and low affinity of their surfaces for water, which determine the amount and rate of water adsorption at particular relative pressure (P/PO), were demonstrated to be responsible for the unusual shapes of the isotherms. The water capacities of these pillared clays were found to be 200-300 mg/g of degassed sample, which are comparable to commercially available desiccants such as zeolites and silica gels. The application of dessicant materials in gas-fired cooling and dehumidification equipments (air conditioning systems) demands an ideal isotherm shape (moderate type I), a quality lacking both in zeolites and silica gels. Pillaring led to improved water adsorption isotherm shape as compared to the original montmorillonite. Further improvement in the shape of isotherm may be achieved by introducing higher degree of hydrophilic or polarity components in these pillared clays.

Original languageEnglish (US)
Pages (from-to)354-362
Number of pages9
JournalSolid State Ionics
Volume32-33
Issue numberPART 1
DOIs
StatePublished - Jan 1 1989

Fingerprint

Bentonite
Steam
montmorillonite
Clay minerals
Oxides
Water vapor
water vapor
isotherms
clays
ceramics
Clay
Adsorption
Isotherms
adsorption
oxides
Water
water
Zeolites
Nitrogen
Silica Gel

All Science Journal Classification (ASJC) codes

  • Chemistry(all)
  • Materials Science(all)
  • Condensed Matter Physics

Cite this

@article{a39ab50c96c242f8b8216e7fba469abd,
title = "Unusual water vapor adsorption behavior of montmorillonite pillared with ceramic oxides",
abstract = "A montmorillonite was pillared with oxide pillars such as Al2O3, ZrO2 and TiO2 to generate permanent microporosity in the interlayers. The X-ray powder diffraction analysis and nitrogen and water adsorption measurements indicated that the pillars were stable at least up to 600°C. The slit widths (pore size) are on the order of 7-9 {\AA} for Al2O3, 8-10 {\AA} for ZrO2 and 14-17 {\AA} for TiO2 pillared clay. The TiO2 pillared clay exhibited Brunauer type IV isotherm that fits BET linear equation for both nitrogen and water. Although Al2O3 and ZrO2 pillared clays followed Brunauer type I isotherm with nitrogen, their water adsorption isotherms exhibited unusual shapes and did not fit either Langmuir or BET equation. The unique pore sizes of these pillared clays and low affinity of their surfaces for water, which determine the amount and rate of water adsorption at particular relative pressure (P/PO), were demonstrated to be responsible for the unusual shapes of the isotherms. The water capacities of these pillared clays were found to be 200-300 mg/g of degassed sample, which are comparable to commercially available desiccants such as zeolites and silica gels. The application of dessicant materials in gas-fired cooling and dehumidification equipments (air conditioning systems) demands an ideal isotherm shape (moderate type I), a quality lacking both in zeolites and silica gels. Pillaring led to improved water adsorption isotherm shape as compared to the original montmorillonite. Further improvement in the shape of isotherm may be achieved by introducing higher degree of hydrophilic or polarity components in these pillared clays.",
author = "P. Malla and S. Yamanaka and Sridhar Komarneni",
year = "1989",
month = "1",
day = "1",
doi = "10.1016/0167-2738(89)90241-5",
language = "English (US)",
volume = "32-33",
pages = "354--362",
journal = "Solid State Ionics",
issn = "0167-2738",
publisher = "Elsevier",
number = "PART 1",

}

Unusual water vapor adsorption behavior of montmorillonite pillared with ceramic oxides. / Malla, P.; Yamanaka, S.; Komarneni, Sridhar.

In: Solid State Ionics, Vol. 32-33, No. PART 1, 01.01.1989, p. 354-362.

Research output: Contribution to journalArticle

TY - JOUR

T1 - Unusual water vapor adsorption behavior of montmorillonite pillared with ceramic oxides

AU - Malla, P.

AU - Yamanaka, S.

AU - Komarneni, Sridhar

PY - 1989/1/1

Y1 - 1989/1/1

N2 - A montmorillonite was pillared with oxide pillars such as Al2O3, ZrO2 and TiO2 to generate permanent microporosity in the interlayers. The X-ray powder diffraction analysis and nitrogen and water adsorption measurements indicated that the pillars were stable at least up to 600°C. The slit widths (pore size) are on the order of 7-9 Å for Al2O3, 8-10 Å for ZrO2 and 14-17 Å for TiO2 pillared clay. The TiO2 pillared clay exhibited Brunauer type IV isotherm that fits BET linear equation for both nitrogen and water. Although Al2O3 and ZrO2 pillared clays followed Brunauer type I isotherm with nitrogen, their water adsorption isotherms exhibited unusual shapes and did not fit either Langmuir or BET equation. The unique pore sizes of these pillared clays and low affinity of their surfaces for water, which determine the amount and rate of water adsorption at particular relative pressure (P/PO), were demonstrated to be responsible for the unusual shapes of the isotherms. The water capacities of these pillared clays were found to be 200-300 mg/g of degassed sample, which are comparable to commercially available desiccants such as zeolites and silica gels. The application of dessicant materials in gas-fired cooling and dehumidification equipments (air conditioning systems) demands an ideal isotherm shape (moderate type I), a quality lacking both in zeolites and silica gels. Pillaring led to improved water adsorption isotherm shape as compared to the original montmorillonite. Further improvement in the shape of isotherm may be achieved by introducing higher degree of hydrophilic or polarity components in these pillared clays.

AB - A montmorillonite was pillared with oxide pillars such as Al2O3, ZrO2 and TiO2 to generate permanent microporosity in the interlayers. The X-ray powder diffraction analysis and nitrogen and water adsorption measurements indicated that the pillars were stable at least up to 600°C. The slit widths (pore size) are on the order of 7-9 Å for Al2O3, 8-10 Å for ZrO2 and 14-17 Å for TiO2 pillared clay. The TiO2 pillared clay exhibited Brunauer type IV isotherm that fits BET linear equation for both nitrogen and water. Although Al2O3 and ZrO2 pillared clays followed Brunauer type I isotherm with nitrogen, their water adsorption isotherms exhibited unusual shapes and did not fit either Langmuir or BET equation. The unique pore sizes of these pillared clays and low affinity of their surfaces for water, which determine the amount and rate of water adsorption at particular relative pressure (P/PO), were demonstrated to be responsible for the unusual shapes of the isotherms. The water capacities of these pillared clays were found to be 200-300 mg/g of degassed sample, which are comparable to commercially available desiccants such as zeolites and silica gels. The application of dessicant materials in gas-fired cooling and dehumidification equipments (air conditioning systems) demands an ideal isotherm shape (moderate type I), a quality lacking both in zeolites and silica gels. Pillaring led to improved water adsorption isotherm shape as compared to the original montmorillonite. Further improvement in the shape of isotherm may be achieved by introducing higher degree of hydrophilic or polarity components in these pillared clays.

UR - http://www.scopus.com/inward/record.url?scp=0024613073&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0024613073&partnerID=8YFLogxK

U2 - 10.1016/0167-2738(89)90241-5

DO - 10.1016/0167-2738(89)90241-5

M3 - Article

AN - SCOPUS:0024613073

VL - 32-33

SP - 354

EP - 362

JO - Solid State Ionics

JF - Solid State Ionics

SN - 0167-2738

IS - PART 1

ER -